Abstract Objectives This study evaluated if the use of a bioactive glass-ceramic-based gel, named Biosilicate (BS), before, after or mixed with bleaching gel, could influence the inflammation of the dental pulp tissue of rats’ molars undergoing dental bleaching with hydrogen peroxide (H2O2). Methodology The upper molars of Wistar rats (Rattus norvegicus, albinus) were divided into Ble: bleached (35% H2O2, 30-min); Ble-BS: bleached and followed by BS-based gel application (20 min); BS-Ble: BS-based gel application and then bleaching; BS/7d-Ble: BS-based gel applications for 7 days and then bleaching; Ble+BS: blend of H2O2 with BS-based gel (1:1, 30-min); and control: placebo gel. After 2 and 30 days (n=10), the rats were euthanized for histological evaluation. The Kruskal-Wallis and Dunn statistical tests were performed (P<0.05). Results At 2 days, the Ble and Ble-BS groups had significant alterations in the pulp tissue, with an area of necrosis. The groups with the application of BS-based gel before H2O2 had moderate inflammation and partial disorganization in the occlusal third of the coronary pulp and were significantly different from the Ble in the middle and cervical thirds (P<0.05). The most favorable results were observed in the Ble+BS, which was similar to the control in all thirds of the coronary pulp (P>0.05). At 30 days, the pulp tissue was organized and the bleached groups presented tertiary dentin deposition. The Ble group had the highest deposition of tertiary dentin, followed by the Ble-BS, and both were different from control (P<0.05). Conclusion A single BS-based gel application beforehand or BS-based gel blended with a bleaching gel minimize the pulp damage induced by dental bleaching.

GlassPanacea is an efficient software tool that combines several attractive technical features with ease of use. Its configuration leads to the intuitive handling and learning with accurate results, providing the users with flexibility in the selection of suitable chemicals for the formulation of glassy, partially glassy or crystalline ceramic materials, as well as speed and accuracy in the calculation of the relative proportions of each chemical in a batch. The software runs directly from an executable file with multiplatform support. Hence, it can be used on different operating systems, such as Windows, Linux and Mac OS, without installation. One of its highlights is the user-friendly interface that enables immediate application, even for operators with little computer experience. This makes GlassPanacea a very valuable tool for students, researchers and engineers who work on the development of ceramic materials using different synthesis techniques, such as melting, solid-state reaction, sintering and sol-gel processing. The archive containing the software, information for use and logo can be downloaded, free of charge, from http://www.certev.ufscar.br/research-1/glasspanacea-glass-and-ceramic-formulation-software.

This paper presents a historical of the Biosilicate®, a bioactive glass-ceramic developed at the Vitreous Materials Laboratory of the Federal University of São Carlos, Brazil. After decades of study accomplished with bioactive glasses and glass-ceramics, Biosilicate® results from a natural evolution and has similar bioactivity index, but far superior mechanical properties than of all bioactive glasses. Biosilicate® is almost fully crystalline and also exhibits much higher bioactivity than all the currently commercially available bioactive glass-ceramics. Due to its special characteristics, Biosilicate® has been successfully tested for several medical and dental applications as we thoroughly discuss in this review paper.

Ceramic matrix composites (CMCs), constituted of a silicon boron oxycarbide (SiBCO) matrix and unidirectional carbon fiber rods as a reinforcement phase, were prepared by pyrolysis of carbon fiber rods wrapped in polysiloxane (PS) or poly(borosiloxane) (PBS) matrices. The preparation of the polymeric precursors involved hydrolysis/condensation reactions of alkoxysilanes in the presence and absence of boric acid, with B/Si atomic ratios of 0.2 and 0.5. Infrared spectra of PBS showed evidence of Si-O-B bonds at 880 cm-1, due to the incorporation of the crosslinker trigonal units of BO3 in the polymeric network. X ray diffraction analyses exhibited an amorphous character of the resulting polymer-derived ceramics obtained by pyrolysis up to 1000 °C under inert atmosphere. The C/SiBCO composites showed better thermal stability than the C/SiOC materials. In addition, good adhesion between the carbon fiber and the ceramic phase was observed by SEM microscopy